Fabrication of ß-Ga2O3 Nanotubes via Sacrificial GaSb-Nanowire Templates.

ß-Ga2O3 nanostructures are attractive wide-band-gap semiconductor materials as they exhibit promising photoelectric properties and potential applications. Despite the extensive efforts on ß-Ga2O3 nanowires, investigations into ß-Ga2O3 nanotubes are rare since the tubular structures are hard to synthesize. In this paper, we report a facile method for fabricating ß-Ga2O3 nanotubes using pre-synthesized GaSb nanowires as sacrificial templates. Through a two-step heating-treatment strategy, the GaSb nanowires are partially oxidized to form ß-Ga2O3 shells, and then, the residual inner parts are removed subsequently in vacuum conditions, yielding delicate hollow ß-Ga2O3 nanotubes. The length, diameter, and thickness of the nanotubes can be customized by using different GaSb nanowires and heating parameters. In situ transmission electron microscopic heating experiments are performed to reveal the transformation dynamics of the ß-Ga2O3 nanotubes, while the Kirkendall effect and the sublimation process are found to be critical. Moreover, photoelectric tests are carried out on the obtained ß-Ga2O3 nanotubes. A photoresponsivity of ~25.9 A/W and a detectivity of ~5.6 × 1011 Jones have been achieved with a single-ß-Ga2O3-nanotube device under an excitation wavelength of 254 nm.

Hydrothermal Synthesis of Te Nanosheets: Growth Mechanism and Electrical Property.

Hydrothermal synthesis is a highly efficient way to yield multiform Te nanosheets. However, the growth mechanisms and property discrepancies between different types of Te nanosheets are still unclear. In this paper, we perform an investigation on this issue by monitoring the hydrothermally synthesized Te nanosheets at different growth stages with transmission electron microscopy and electrical tests. Three main types of Te nanosheets and their variants are revealed including trapezoidal and "V"-shaped configurations. It is found that the different types of Te nanosheets dominate at different reaction stages, indicating a sequential growth scenario. Surfactants and surface energy co-determine the growth kinetics, while the crystallographic attachments lead to specifically included angles of 74° and 41° in the "V"-shaped Te nanosheets. The fractions of the three main types of Te nanosheets as a function of reaction time are statistically tracked, and their crystalline structures, interfaces, and preferential growth orientations are uncovered. Moreover, the electrical properties of the Te nanosheets are tested, and the results show an interface-related feature. These findings provide some new insights into the synthesis and property of low-dimensional Te functional materials.